Modeling and Evaluation of Moisture Diffusion in Polymer Composite Materials
Başlık:
Modeling and Evaluation of Moisture Diffusion in Polymer Composite Materials
Yazar:
Huo, Zhen, author.
ISBN:
9780438115828
Yazar Ek Girişi:
Fiziksel Tanımlama:
1 electronic resource (133 pages)
Genel Not:
Source: Dissertation Abstracts International, Volume: 79-11(E), Section: B.
Advisors: K. Chandrashekhara Committee members: Xiaoping Du; Ming C. Leu; Thomas Schuman; Lesley H. Sneed.
Özet:
Fiber-reinforced polymer composites have extensive applications due to their high specific strength, improved product performance, low maintenance and design flexibility. However, moisture absorbed by polymer composites during the service life plays a detrimental role in both the integrity and durability of composite structure. It is essential to understand the moisture diffusion behavior and induced damage in polymer matrix composites under varying hygrothermal conditions. In Part I, the moisture diffusion characteristics in hybrid composites using moisture concentration-dependent diffusion method have been investigated. Also, a multi-stage diffusion model was proposed to explain the deviation of moisture diffusion behavior for sandwich composites from classical Fick's law using a time-dependent diffusivity scheme. User-defined subroutines were developed to implement these methods into commercial finite element code. To validate the simulation results, an open-edge moisture diffusion experiment was conducted for sandwich composites composed of woven E-glass fiber-reinforced polyurethane (PU) face sheets and a closed-cell rigid PU foam core. In Part II, the behavior of moisture diffusion and its effects on the mechanical properties of carbon/bismaleimide composites exposed to seawater conditioning at elevated temperatures were investigated. The degradation of mechanical properties due to hygrothermal aging was assessed by conducting short beam shear test and flexural test at three immersion time points. In Part III, the effect of moisture on mechanical performance of PU sandwich composites was investigated. Mechanical property degradation due to moisture absorption was evaluated by conducting compression test of the foam core, flexural test of the laminates, and double cantilever beam Mode-I interfacial fracture test of sandwich composites.
Notlar:
School code: 0587
Tüzel Kişi Ek Girişi:
Mevcut:*
Yer Numarası | Demirbaş Numarası | Shelf Location | Lokasyon / Statüsü / İade Tarihi |
---|---|---|---|
XX(687606.1) | 687606-1001 | Proquest E-Tez Koleksiyonu | Arıyor... |
On Order
Liste seç
Bunu varsayılan liste yap.
Öğeler başarıyla eklendi
Öğeler eklenirken hata oldu. Lütfen tekrar deneyiniz.
:
Select An Item
Data usage warning: You will receive one text message for each title you selected.
Standard text messaging rates apply.