Diffuse Boundary Layer Effects on the Properties of Metal in Metal Matrix Composites Manufactured with the Field Assisted Sintering Technique
Başlık:
Diffuse Boundary Layer Effects on the Properties of Metal in Metal Matrix Composites Manufactured with the Field Assisted Sintering Technique
Yazar:
Hooke, Ryan Thomas, author.
ISBN:
9780438099852
Yazar Ek Girişi:
Fiziksel Tanımlama:
1 electronic resource (449 pages)
Genel Not:
Source: Dissertation Abstracts International, Volume: 79-10(E), Section: B.
Özet:
The focus of this thesis is the effect of diffuse boundary layers on overall material failure in a tungsten heavy alloy (WHA) and D2 tool steel composite. D2 tool steel powder was sintered and joined to macroscopic WHA material using field assisted sintering, where high DC fields are introduced during the consolidation process. Diffuse boundary layers were formed during the field assisted sintering of the metal in metal matrix. To investigate the failure mechanisms, bulk and localized material properties of the metal in metal matrix composites were determined, including impact energy and hardness and findings suggest the diffusion zone is not uniformly thick. The diffusion zone is approximately 40-50 microm thick. Mechanical properties are generally bilaterally affected 30-40 microm deep into the WHA compared to wrought, but can also be affected up to 10 microm into the D2 steel, while the impact toughness of the composite is close to that of wrought D2 tool steel.
Material specimens were processed using equipment located at US Army RDECOM ARDEC. The resulting microstructures were examined using optical and scanning electron microscopy. Mechanical properties and failure properties were measured using equipment located at Rutgers University and US Army RDECOM ARDEC. The mechanical properties were evaluated at room temperature using custom impact testing and nanoindentation. Failure modes were examined with respect to metal boundary separation, crack initiation, and propagation due to strain, at, in, or near the diffusion affected zone and onset of fracture was found to occur at the interface as well as in the bulk WHA.
These methods and data were used in the determination of constitutive model parameters. A validation of model parameters was completed with an explicit finite element model of the composite configurations. Initial assessments of damage were modeled using Johnson-Cook material and damage models. The models were refined and results represent fracture location, deformation, and failure modes.
Notlar:
School code: 0190
Konu Başlığı:
Mevcut:*
Yer Numarası | Demirbaş Numarası | Shelf Location | Lokasyon / Statüsü / İade Tarihi |
---|---|---|---|
XX(687310.1) | 687310-1001 | Proquest E-Tez Koleksiyonu | Arıyor... |
On Order
Liste seç
Bunu varsayılan liste yap.
Öğeler başarıyla eklendi
Öğeler eklenirken hata oldu. Lütfen tekrar deneyiniz.
:
Select An Item
Data usage warning: You will receive one text message for each title you selected.
Standard text messaging rates apply.